| Property | Test method | Conditions | Value |
| Physical and Mechanical | |||
| Cont. service temp. | IEC 60216 | 20000h | 90°C |
| Density | ASTM D792 | 1.3 g/cm³ | |
| Elongation at break | ASTM D638 | 450% | |
| Hardness shore | ASTM D2240 | 88A | |
| Radiation resistance | IEC 60544 | 10^7 Gy | |
| Temperature range | -40°C to 100°C | ||
| Tensile strength at break | ASTM D638 | 37 MPa | |
| Electrical | |||
| Dielectric constant | DIN53483/VDE0303 p.4 | 50 Hz | 8 |
| Dissipation factor | DIN53483/VDE0303 p.4 | 50 Hz | 0.04 |
| Volume resistivity | DIN53482/VDE0303 p.3 | 10^11 ohm·cm | |
| Flammability | |||
| Combustion corrosivity | IEC 60754-2 | pH 6.2/ 16uS/mm | |
| Flame retardancy | IEC 60332-1 | pass | |
| Flammability | UL 94 | 1.6 mm | V-0 |
| Oxygen index | ASTM D2863 | 25% | |
| Smoke index | NF F 16-101 | 28.1 (class F2) | |
| Smoke index | NES 711 | per 100 g | 61 |
| Temperature index | NES 715 | 174 °C | |
| Toxicity index | NF X 70-100 | 600ºC | 10.4 |
| Toxicity index | NES 713 | per 100g | 5 |
| Chemical | |||
| Acids | good |
||
| Bases | fair | ||
| Fuels | good |
||
| Oils | excellent |
IMPORTANT
Habia Cable has compiled the information contained herein from what it believes are authoritative sources and believes that is accurate and factual as of the date printed.
It is offered solely as a convenience to its customers and is intended only as a guide concerning the materials mentioned.
Any changes in the data sheet will be made without notification.
Habia Cable has compiled the information contained herein from what it believes are authoritative sources and believes that is accurate and factual as of the date printed.
It is offered solely as a convenience to its customers and is intended only as a guide concerning the materials mentioned.
Any changes in the data sheet will be made without notification.
Internet ...................... www.habia.com
Email ........................ info@habia.com
International Telephone .....+46 (0) 293 22000